Color-coated sheet is based on galvanized sheet, galvalume sheet, zinc-aluminum-magnesium, aluminum-zinc-magnesium, aluminum-magnesium-manganese, stainless steel as the substrate, after surface pretreatment, using a roller coating method, coated with multiple layers of liquid paint, after baking Bake and cool.It uses polyester, silicon-modified polyester, high-weather-resistant polyester, polyvinylidene fluoride, epoxy, and high-sealing corrosion-resistant coatings. It has excellent durability, corrosion resistance, and moldability（formability）. Products are widely used in household appliances, decoration, construction, automotive and other industries.

Product name Color Coated Steel Coil
Grade TSGCC/TDX51D/TDX52D
Thickness 0.09-2.0mm
Width 750-1250mm
Coil Weight 2-10T
Coil ID 508/610mm
Top coating thickness 10-30um
Back coating thickness 5-25um
Paint type PE/SMP/HDP/PVDF
Base matenal GI/GL/GA/AL/STS
Color All RAL colors or customers samples color
Annual production capacity 1000000T
Place of Origin Shandong, China
Production Standard EN/GB/AISI/ASTM/DIN/JIS
Delivery Time 7-15 days/According to customer requirements
Brand Name Xinhe
Certificate ISO9001/ISO14001/ISO45001
Payment FOB 30% deposit,70% before shipment
Quality assurance According to the order requirements
Packaging requirements According to the order requirements
Product Name Film thicknessμm Core performance T bend MEK Neutral salt spray QUV-A Recommended environment
Self-cleaning products ≥25 Carbon black experiment △E＜2, water contact angle ≥30 degrees 2T ≥100 1000 h 3000 h C3 level environment
Heat reflection products ≥25 TSR≥0.25，SRI：Light color≥78，other colours≥29 2T ≥100 1000 h 1500 h C3 level environment
Anti-static products ≥25 Surface resistance 1066-1099Ω 2T ≥100 1000 h 1500 h C2 level environment
Antibacterial products ≥25 Activity against Staphylococcus aureus and E. coli＞2 2T ≥100 1000 h 1500 h C2 level environment
Type of coating Recommended substrate type Coating thicknessμm MEK T bend Porosity 5%hydrochloric acid 5%Sodium hydroxide Neutral salt spray Acid salt spray Alkaline salt spray QUV-A Common environment Dedicated environment Recommended environment
Polyester（PE） Z/AZ/ZM/AZM ≥20 ≥100 3T / 24 h 24 h 1000 h / / 1000 h 10 year / C2 environment
High weather resistance（HDP） Z/AZ/ZM/AZM ≥23 ≥100 3T / 24 h 24 h 1500 h / / 1500 h 15 year / C3 environment
Silicon Reform（SMP） Z/AZ/ZM/AZM ≥23 ≥100 3T / 24 h 24 h 1500 h / / 1500 h 15 year / C2 environment
Fluorocarbon（PVDF） Z/AZ/ZM/AZM ≥25 ≥100 2T / 24 h 24 h 2000 h / / 3000 h 20~30 year / C4 environment
Polyurethane（PU） Z/AZ/ZM/AZM ≥40 ≥100 2T / 24 h 24 h 720 h / / 1000 h 10~20 year / C2 environment
Hot film（VCM） Z/AZ/ZM/AZM ≥100 / 0T / 360 h / / / / / 10 year / C2 environment
Color printing Z/AZ/ZM/AZM ≥25 ≥100 3T / 24 h 24 h 600 h / / 1000 h 10 year / C2 environment
Reticulated, suede Z/AZ/ZM/AZM ≥25 ≥100 2T / 24 h 24 h 1000 h / / 1000 h 10 year / C2 environment
High corrosion-resistant polyester Z/ZM/AZM ≥25 ≥1000 3T 90V No breakdown 120 h 120 h 2000 h 1500 h 1500 h 2000 h 15 year 10 year C5 environment
（PE•Pro）
High corrosion resistance and weather resistance polyester（HDP•Pro） Z/ZM/AZM ≥25 ≥1000 3T 90V No breakdown 120 h 120 h 2500 h 2000 h 2000 h 3000 h 20 year 15 year C5 environment
Super corrosion resistant super weather resistant polyester（HDP•Plus） Z/ZM/AZM ≥30 ≥1000 3T 90V No breakdown 360 h 360 h 4000 h 3000 h 3000 h 4000 h 25 year 20 year C5 environment
High corrosion resistance fluorocarbon aluminum magnesium manganese（PVDF•Pro） Aluminum magnesium manganese ≥25 ≥1000 2T 90V No breakdown 240 h 240 h 10000 h 5000 h 5000 h 10000 h 50 year / Key industrial engineering,
National public projects
Super corrosion-resistant nano-fluorocarbon aluminum magnesium manganese（PVDF•Plus） Aluminum magnesium manganese ≥30 ≥1000 2T 90V No breakdown 480 h 480 h 20000 h 10000 h 10000 h 15000 h 70 year / Key industrial engineering,
National public projects
Centennial stainless steel fluorocarbon（PVDF•Plus） Stainless steel ≥30 ≥1000 2T 90V No breakdown 480 h 480 h 30000 h 10000 h 10000 h 15000 h 100 year / Key industrial engineering,
National public projects
High corrosion-resistant epoxy back paint / ≥12 ≥100 4T 67.5V No breakdown 120 h 120 h 2000 h 1500 h 1500 h / / / Supporting the use of
Super corrosion-resistant epoxy back paint / ≥20 ≥100 3T 90V No breakdown 240 h 240 h 3000 h 2500 h 2500 h 2000 h / / Supporting the use of

Product Details

1）color coated galvanized steel coil

On the continuous unit, the galvanized steel strip and the galvanized steel strip (electro-galvanized and hot-dip galvanized) are used as the substrate, and the surface is pretreated (degreased and learned) and then coated with one or more layers by the method of roller coating. Liquid paint, the plate obtained after baking and cooling, is the coated steel plate.

2）Production process

Welding →Inlet Looper→Pre-treatment→Primer coat→Baking→Cooling→Uncoiling→Finish coat→Baking→Embossed or film→QC→Coiling.

3) COILS TEST

Paint thickness:10-30um as your require

Glossy: Highlight(70-95), Matte(lower than 40), Medium gloss(40-60) as your requirment.

T-bending:0-3T as required

Wipe: can reach 200 times

Natural Salt Spray: More than 1000 hours. It is decided by paint thickness and different paint.PE more than 1000 hours.HDP more than 1500 hours. PVDF more than 2000 hours.

UV light experiment: for regular paint, not less than 500 hours.For matt and high paint, not less than 1000 hours

Our Advantage

15years experience
Free sample offered
6 product-lines
exported to 60+ countries
Factory direct supply
7*24 Professional service

Wrapped by plastic film and waterproof paper, iron sheet, and iron waist for outer packaging.

With wooden pallets for film coils and wrinkle coils. Or as your requested.

Contact us Form

"*" indicates required fields

This field is for validation purposes and should be left unchanged.

RELATED PRODUCTS

Mirror Steel Plate

Pattern Steel Plate

Stainless Steel Coil

Stainless Steel Strip

Steel plate punching